The new mineral naalasite (IMA2023–027), NaAl(AsO3OH)2⋅H2O, was found at the Torrecillas mine, Iquique Province, Chile, where it is a secondary alteration phase associated with anhydrite, juansilvaite, magnesiokoritnigite and a lavendulan-like phase. Naalasite occurs in tightly intergrown aggregates and druses of equant crystals. Crystals are light to medium pink and transparent, with vitreous lustre and white streak. The Mohs hardness is ~3½. The density is 3.19(2) g⋅cm–3. Optically, naalasite is uniaxial (+), with ω = 1.630(3) and ɛ = 1.660(3) (white light). The empirical formula (based on 9 O apfu) is Na0.92Al0.61Fe3+0.39As2O9H4.07. Naalasite is trigonal, space group R32, with cell parameters: a = 8.494(4), c = 26.430(13) Å, V = 1651.5(4) Å3 and Z = 9. The structure, refined to R1 = 3.78% for 641 I > 2σI reflections, is based on a loose 3D framework of alternating AsO3OH tetrahedra and AlO6 octahedra. The structure is topologically equivalent to that of nafeasite and can be regarded as its Al analogue, even though nafeasite is monoclinic with space group C2.

The new mineral nafeasite (IMA2021-103), NaFe3+(AsO3OH)2⋅H2O, was found at the Torrecillas mine, Iquique Province, Chile, where it is a secondary alteration phase associated with anhydrite, gypsum, halite, lavendulan, magnesiokoritnigite and natrojarosite. Nafeasite occurs in tightly intergrown aggregates of equant crystals. Crystals are light to medium pink and transparent, with vitreous lustre and white streak. The Mohs hardness is ~2½. The density is 3.23(2) g⋅cm–3. Optically, nafeasite is biaxial (+), with α = 1.679(3), β = 1.682(3), γ = 1.730(5) (white light); 2V = 27(2)°; and slight r < v dispersion. The empirical formulae of the holotype and cotype (based on 9 O atoms per formula unit) are Na0.98K0.02Fe0.92Al0.07As2.00O9H4.01 and Na0.97Fe0.68Al0.33As2.00O9H4.01, respectively. Nafeasite is monoclinic, space group C2, with cell parameters: a = 18.6876(16), b = 8.6769(7), c = 14.8100(10) Å, β = 105.238 (5)°, V = 2317.0(3) Å3 and Z = 12. The structure, refined to R1 = 5.03% for 5979 Io > 2σI reflections, is based on a loose 3D framework of alternating AsO3OH tetrahedra and Fe3+O6 octahedra.

The new mineral mauriziodiniite (IMA2019-036), NH4(As2O3)2I, was found at the Torrecillas mine, Iquique Province, Chile, where it is a secondary alteration phase associated with calcite, cuatrocapaite-(NH4), lavendulan, magnesiokoritnigite and torrecillasite on matrix consisting of native arsenic, arsenolite and pyrite. Mauriziodiniite occurs as hexagonal tablets up to ~300 μm in diameter. Crystals are colourless and transparent, with pearly to adamantine lustre and white streak. The Mohs hardness is ~1. Tablets are sectile and easily flexible, but not elastic. Fracture is curved, irregular and stepped. Cleavage is perfect on {001}. The calculated density is 3.916 g/cm3. Optically, mauriziodiniite is uniaxial (–) with ω = 2.07(calc) and ɛ = 1.770(5) (white light). The empirical formula, determined from electron microprobe analyses, is (NH4)0.94K0.03(As2O3)2I0.92Cl0.03. Mauriziodiniite is hexagonal, P6/mmm, a = 5.289(2), c = 9.317(2) Å, V = 225.68(18) Å3 and Z = 1. The structure, refined to R1 = 4.16% for 135 Io > 2σI reflections, contains three types of layers: (1) a planar neutral As2O3 (arsenite) sheet; (2) an NH4+ layer that links adjacent arsenite sheets via bonds to their O atoms; and (3) an I– layer that links adjacent arsenite sheets via bonds to their As atoms. The layer sequence is I–As2O3–NH4–As2O3–I. Mauriziodiniite is isostructural with lucabindiite and is structurally related to gajardoite, cuatrocapaite-(NH4), cuatrocapaite-(K) and torrecillasite.

The new minerals camanchacaite, NaCaMg2[AsO4]2[AsO3(OH)2], chinchorroite, Na2Mg5(As2O7)2(AsO3OH)2(H2O)10, espadaite, Na4Ca3Mg2[AsO3(OH)]2[AsO2(OH)2]10(H2O)6·H2O, magnesiofluckite, CaMg(AsO3OH)2(H2O)2, picaite, NaCa[AsO3OH][AsO2(OH)2] and ríosecoite, Ca2Mg(AsO3OH)3(H2O)2, were discovered on two closely related specimens collected from the Torrecillas mine, Iquique Province, Chile. These minerals occur as secondary phases on massive quartz–hematite also in association with anhydrite, gypsum, halite and talmessite. Camanchacaite is monoclinic, C2/c, a = 12.470(9), b = 12.554(9), c = 6.848(9) Å, β = 113.75(2)°, V = 981.3(16) Å3 and Z = 4. It has a protonated alluaudite-type structure. Chinchorroite is triclinic, P$\bar{1}$, a = 8.7777(2), b = 8.8570(3), c = 9.7981(7) Å, α = 91.097(6), β = 110.544(8), γ = 103.167(7)°, V = 690.43(7) Å3 and Z = 1. The structure contains abbreviated chains of five edge-sharing Mg octahedra that are linked by pyroarsenate and hydrogen-arsenate groups. Espadaite is orthorhombic, Ccca, a = 12.3649(10), b = 22.181(2), c = 18.3292(13) Å, V = 5027.1(7) Å3 and Z = 4. The structure is based on heteropolyhedral sheets of formula {Ca3Mg2[AsO3(OH)]2[AsO2(OH)2]10}4− that contain large voids; NaO6 polyhedra occupy the interlayer region. Magnesiofluckite is triclinic, P$\bar{1}$, a = 8.4143(6), b = 7.5321(5), c = 6.8917(4) Å, α = 82.477(6), β = 97.682(6), γ = 95.379(6)°, V = 427.84(5) Å3 and Z = 2. It is isostructural with fluckite. Picaite is monoclinic, P21/c, a = 7.2474(4), b = 14.6547(7), c = 7.2624(5) Å, β = 99.520(7)°, V = 760.70(8) Å3 and Z = 4. The structure contains chains of edge-sharing Na− and Ca octahedra with bridging AsO3(OH) and AsO2(OH)2 tetrahedra. Ríosecoite is triclinic, P$\bar{1}$, a = 6.8110(9), b = 7.3156(12), c = 11.7773(17) Å, α = 83.466(6), β = 84.394(6), γ = 79.779(6)°, V = 571.95(15) Å3 and Z = 2. The structure contains tetramers of edge-sharing CaO7 and CaO8 polyhedra linked by MgO6 octahedra and bridging AsO3(OH) groups to form chains.

The new minerals cuatrocapaite-(NH4) (IMA2018-083) and cuatrocapaite-(K) (IMA2018-084) are the NH4- and K-dominant members of a series with the general formula (NH4,K)3(NaMg□)(As2O3)6Cl6·16H2O. Both minerals were found at the Torrecillas mine, Iquique Province, Chile, where they occur as secondary alteration phases. Both minerals occur as hexagonal tablets up to ~0.3 mm in diameter. They are transparent, with a vitreous lustre and white streak. For both, the Mohs hardness is ca. 2½, the crystals are somewhat flexible, but not elastic, the fracture is irregular and the cleavage is perfect on {001}. The measured densities are 2.65(2) and 2.76(2) g/cm3 for the NH4- and K-dominant species, respectively. Optically, cuatrocapaite-(NH4) is uniaxial (–) with ω = 1.779(3) and ε = 1.541(3) and cuatrocapaite-(K) is uniaxial (–) with ω = 1.777(3) and ε = 1.539(3) (white light). The minerals are insoluble in acids, but decompose in NaOH(aq). The empirical formulas, determined from electron-microprobe analyses, are (NH4)2.48Na1.66Mg0.87K0.09(As12O18.05)Cl5.88·16.02H2O and K2.68Na1.33Mg0.93(NH4)0.31(As12O18.01)Cl6.16·16.04H2O. The minerals are trigonal, space group R${\bar 3}$m; the cuatrocapaite-(NH4) cell parameters are a = 5.25321(19), c = 46.6882(19) Å, V = 1115.80(9) Å3 and Z = 1; the cuatrocapaite-(K) cell parameters are a = 5.2637(15), c = 46.228(8) Å, V = 1109.2(7) Å3 and Z = 1. The structures, refined for cuatrocapaite-(NH4) to R1 = 1.78% for 544 Io > 2σI reflections, contain four types of layers: (1) a planar neutral As2O3 (arsenite) sheet; (2) an (${\rm NH}_{\rm 4}^{\vskip -2pt\rm \scale65% +} $,K+) layer that links adjacent arsenite sheets; (3) a Cl– layer placed on the As side of each arsenite; and (4) a layer containing partially occupied Na, Mg and H2O sites that is flanked on either side by Cl layers. The layer sequence for the type 1, 2 and 3 layers is identical to the Cl–As2O3–K–As2O3–Cl layer sequence in the structures of lucabindiite and gajardoite.

The new mineral canutite (IMA2013-070), NaMn3[AsO4][AsO3(OH)]2, was found at two different locations at the Torrecillas mine, Salar Grande, Iquique Province, Chile, where it occurs as a secondary alteration phase in association with anhydrite, halite, lavendulan, magnesiokoritnigite, pyrite, quartz and scorodite. Canutite is reddish brown in colour. It forms as prisms elongated on [20 ] and exhibiting the forms {010}, {100}, {10}, {201} and {102}, or as tablets flattened on {102} and exhibiting the forms {102} and {110}. Crystals are transparent with a vitreous lustre. The mineral has a pale tan streak, Mohs hardness of 2½, brittle tenacity, splintery fracture and two perfect cleavages, on {010} and {101}. The calculated density is 4.112 g cm−3. Optically, canutite is biaxial (+) with α = 1.712(3), β = 1.725(3) and γ = 1.756(3) (measured in white light). The measured 2V is 65.6(4)°, the dispersion is r < v (slight), the optical orientation is Z = b; X ^ a = 18° in obtuse β and pleochroism is imperceptible. The mineral is slowly soluble in cold, dilute HCl. The empirical formula (for tabular crystals from near the mineshaft), determined from electron - microprobe analyses, is (Na1.05Mn2.64Mg0.34Cu0.14Co0.03)∑4.20As3O12H1.62. Canutite is monoclinic, C2/c, a = 12.3282(4), b = 12.6039(5), c = 6.8814(5) Å, β = 113.480(8)°, V = 980.72(10) Å3 and Z = 4. The eight strongest X-ray powder diffraction lines are [d obs Å(I)(hkl)]: 6.33(34)(020), 4.12(26)(21), 3.608(29)(310,31), 3.296(57)(12), 3.150(28)(002,131), 2.819(42)(400,041,330), 2.740(100)(240,02,112) and 1.5364(31)(multiple). The structure, refined to R 1 = 2.33% for 1089 F o > 4σF reflections, shows canutite to be isostructural with protonated members of the alluaudite group.

The new mineral torrecillasite (IMA2013-112), Na(As,Sb)43+O6Cl, was found at the Torrecillas mine, Iquique Province, Chile, where it occurs as a secondary alteration phase in association with anhydrite, cinnabar, gypsum, halite, lavendulan, magnesiokoritnigite, marcasite, quartz, pyrite, scorodite, wendwilsonite and other potentially new As-bearing minerals. Torrecillasite occurs as thin colourless prisms up to 0.4 mm long in jack-straw aggregates, as very thin fibres in puff balls and as massive intergrowths of needles. Prisms are elongated on [100] with diamond-shaped cross-section and irregular terminations. Crystals are transparent, with adamantine lustre and white streak. The Mohs hardness is 2½, tenacity is brittle and fracture is irregular. Cleavage on (001) is likely. The calculated density is 4.056 g cm−3. Optically, torrecillasite is biaxial (−) with α = 1.800(5), β = 1.96(1), γ = 2.03(calc.) (measured in white light). The measured 2V is 62.1(5)°, no dispersion or pleochroism were observed, the optical orientation is X = c, Y = b, Z = a. The mineral is very slowly soluble in H2O, slowly soluble in dilute HCl and rapidly soluble in concentrated HCl. The empirical formula, determined from electron-microprobe analyses, is (Na1.03Mg0.02)∑1.05(As3.39Sb0.62)∑4.01O6.07Cl0.93. Torrecillasite is orthorhombic, Pmcn, a = 5.2580(9), b = 8.0620(13), c = 18.654(3) Å, V = 790.7(2) Å3 and Z = 4. The eight strongest X-ray powder diffraction lines are [dobs Å(I)(hkl)]: 4.298(33)(111), 4.031(78)(014,020), 3.035(100)(024,122), 2.853(39)(115,123), 2.642(84)(124,200), 2.426(34)(125), 1.8963(32)(225) and 1.8026(29)(0·1·10,233). The structure, refined to R1 = 4.06% for 814 Fo >4σF reflections, contains a neutral, wavy As2O3 layer parallel to (001) consisting of As3+O3 pyramids that share O atoms to form six-membered rings. Successive layers are flipped relative to one another and successive interlayer regions contain alternately either Na or Cl atoms. Torrecillasite is isostructural with synthetic orthorhombic NaAs4O6Br.

The new mineral magnesiokoritnigite (IMA 2013-049), ideally Mg(AsO3OH)·H2O, was found at the Torrecillas mine, Salar Grande, Iquique Province, Chile, where it occurs as a secondary alteration phase in association with anhydrite, chudobaite, halite, lavendulan, quartz and scorodite. Crystals of magnesiokoritnigite are colourless to pale-pink, thin to thick laths up to 2 mm long. Laths are elongated on [001], flattened on {010} and exhibit the forms {010}, {110}, {10}, {101}, {031} and {01}. The crystals also occur in dense deep-pink intergrowths. Crystals are transparent with a vitreous lustre. The mineral has a white streak, Mohs hardness of ∼3, brittle tenacity, conchoidal fracture and one perfect cleavage on {101}. The measured and calculated densities are 2.95(3) and 2.935 g cm– 3, respectively. Optically, magnesiokoritnigite is biaxial (+) with α = 1.579(1), β = 1.586(1) and γ = 1.620(1) (measured in white light). The measured 2V is 50(2)° and the calculated 2V is 50°. Dispersion is r < v, medium. The optical orientation is Y ≈ b; Z ^ c = 36° in obtuse β (note pseudomonoclinic symmetry). The mineral is non-pleochroic. The empirical formula, determined from electron-microprobe analyses, is (Mg0.94Cu0.03Mn0.02Ca0.01)Σ 1.00As0.96O5H3.19. Magnesiokoritnigite is triclinic, P, with a = 7.8702(7), b = 15.8081(6), c = 6.6389(14) Å, α = 90.814(6), β = 96.193(6), γ = 90.094(7)°, V = 821.06(19) Å3 and Z = 8. The eight strongest X-ray powder diffraction lines are [dobs Å (I)(hkl)]: 7.96(100)(020), 4.80(54)(101), 3.791(85)(10,210,1,31), 3.242(56)(02,1,012), 3.157(92)(21,30,230), 3.021(61)(11,141,21,221), 2.798(41)(02,032) and 1.908(43)(multiple). The structure, refined to R1 = 5.74% for 2360 Fo > 4σF reflections, shows magnesiokoritnigite to be isostructural with koritnigite and cobaltkoritnigite.

The new mineral magnesiocanutite (IMA2016-057), NaMnMg2[AsO4]2[AsO2(OH)2], was found at the Torrecillas mine, Iquique Province, Chile, where it occurs as a secondary phase in association with anhydrite, canutite, halite, lavendulan and magnesiokoritnigite. Magnesiocanutite occurs as pale brownish-pink to rose-pink, lozenge-shaped tablets that are often grouped in tightly intergrown aggregates. The crystal forms are {110} and {102}. Crystals are transparent, with vitreous lustre and white to very pale pink streak. The Mohs hardness is 2½, tenacity is brittle, and the fracture is splintery. Crystals exhibit two perfect cleavages: {010} and {101}. The calculated density is 3.957 g/cm3. Optically, magnesiocanutite is biaxial (+), with α = 1.689(2), β = 1.700(2), γ = 1.730(2) (measured in white light); 2Vmeas. = 64.3(4)°; slight dispersion, r <v; orientation Z = b; X ∧ a = 15° in obtuse angle β. The mineral is slowly soluble in dilute HCl at room temperature. Electron-microprobe analyses, provided Na2O 5.44, CaO 0.26, MgO 8.84, MnO 18.45, CoO 1.47, CuO 2.13, As2O5 59.51, H2O(calc) 2.86, total 98.96 wt.%. Magnesiocanutite is monoclinic, C2/c, a = 12.2514(8), b = 12.4980(9), c = 6.8345(5) Å, β = 113.167(8)°, V = 962.10(13) Å3 and Z = 4. The eight strongest powder X-ray diffraction lines are [dobs Å(I )(hkl)]: 6.25(42)(020), 3.566(43)(310,1̄31), 3.262(96)(1̄12), 3.120(59)(002,131,040,221), 2.787(93)(400,022,041,330), 2.718(100) (4̄21,240,112,402), 2.641(42)(1̄32) and 1.5026(43)(multiple). Magnesiocanutite has a protonated alluaudite-type structure (R1 = 2.59% for 789 Fo > 4σF reflections) and is the Mg analogue of canutite. Using the results of both the microprobe analyses and structure refinement, the structurally based empirical formula is Na(Mn0.78Mg0.22)Σ1.00(Mg1.04Mn0.70Cu0.15Co0.11)Σ2.00[AsO4]2[AsO2(OH)2].

The new mineral juansilvaite (IMA2015-080), Na5Al3[AsO3(OH)]4[AsO2(OH)2]2(SO4)2·4H2O, was foOptically, juansilvaiteund at the Torrecillas mine, Iquique Province, Chile, where it occurs as asecondary alteration phase in association with anhydrite, canutite, halite, sulfur and a mahnertite-like phase. Juansilvaite occurs as bright pink blades up to ∼0.5 mm long grouped in tightly intergrown radial aggregates and also as opaque dull pale pink rounded aggregates. Blades areflattened on {001}, elongated on [100] and exhibit the forms {001}, {111} and {201}. Crystals are transparent, with vitreous lustre and white streak. The Mohs hardness is ∼2½, tenacity is brittle and fracture is irregular. Cleavage is very good on {001}. The measured density is3.01(2) g cm–3 and the calculated density is 3.005 g cm–3. Optically, juansilvaite is biaxial (+) with α= 1.575(1), β = 1.597(1), γ= 1.623(1) and 2V = 86(1)° (measured in white light). Dispersion is r < v, slight, andthe orientation is X = b; Z ^ c = 27° in the obtuse angle β. The pleochroism is X > Y ≈ Z in shades of pale pink. The mineral is slowly soluble in dilute HCl at room temperature. The empirical formula, determined from electron-microprobeanalyses, is Na4.95Al2.28Fe0.503+Mn0.213+Cu0.04As5.92S1.83O36H17.37. Juansilvaite is monoclinic, C2/c, a = 18.1775(13), b = 8.6285(5), c= 18.5138(13) Å, β = 90.389(6)°, V = 2903.7(3) Å3 and Z = 4. The eight strongest powder X-ray diffraction lines are [dobs Å(I)(hkl)]: 9.25(100)(002), 7.20(34)(111), 4.545(34)(400), 3.988(39)(114), 3.363(42)(314), 3.145(66)(512,420), 2.960(68)(422,422) and 2,804(33)(131,423). The structure of juansilvaite (R1 = 3.82% for 2040 Fo > 4σF reflections) contains layers made up of alternating corner-linked Al–O octahedra and acid-arsenate tetrahedra. Sodium cations occur both peripheral to the layers and within cavities in the layers. An SO4 tetrahedron and an H2O group also are in the interlayer region.

The new mineral currierite (IMA2016-030), Na4Ca3MgAl4(AsO3OH)12·9H2O, was found at the Torrecillas mine, Iquique Province, Chile, where it occurs as a secondary alteration phase in association with anhydrite, canutite, chudobaite, halite, lavendulan, magnesiokoritnigite, quartz, scorodite and torrecillasite. Currierite occurs as hexagonal prisms, needles and hair-like fibres up to ∼200 μm long, in sprays. The crystal forms are ﹛100﹜ and ﹛001﹜. Crystals are transparent, with vitreous to silky lustre and white streak. The Mohs hardness is ∼2, tenacity is brittle, but elastic in very thin fibres, and the fracture is irregular. Crystals exhibit at least one good cleavage parallel [001]. The measured density is 3.08(2) g cm -3 and the calculated density is 3.005 g cm -3. Optically, currierite is uniaxial (–) with ω= 1.614(1) and ε= 1.613(1) (measured in white light). The mineral is slowly soluble in dilute HCl at room temperature. The empirical formula, determined from electron-microprobe analyses, is (Na3.95A12.96Ca2.74Mg1.28Fe0.633+Cu0.13K0.08Co0.03Σ11.80 (AS11.685+Sb0.325+Σ12(O56.96Cl0.04)Σ57H30.81. Currierite is hexagonal, P622, with a = 12.2057(9), c = 9.2052(7) Å, V= 1187.7(2) Å3 and Z = 1. The eight strongest powder X-ray diffraction lines are [dobs Å(I)(hkl)]: 10.63(100)(100), 6.12(20)(110), 5.30(15)(200), 4.61(24)(002), 4.002(35)(210), 3.474(29)(202), 3.021(96)(212) and 1.5227(29)(440,334,612). The structure of currierite (R1 = 2.27% for 658 Fo > 4σF reflections) is based upon a heteropolyhedral chain along c in which AlO6 octahedra are triple-linked by sharing corners with AsO3OH tetrahedra. Chains are linked to one another by bonds to 8(4 + 4)-coordinated Na and 8-coordinated Ca forming a three-dimensional framework with large cavities that contain rotationally disordered Mg(H2O)6 octahedra. The chain in the structure of currierite is identical to that in kaatialaite and a geometrical isomer of that in ferrinatrite. The mineral is named in honour of Mr. Rock Henry Currier (1940–2015), American mineral dealer, collector, author and lecturer.

The new mineral gajardoite (IMA2015-040), KCa0.5As3+4O6Cl2·5H2O, was found at the Torrecillas mine, Iquique Province, Chile, where it occurs as a secondary alteration phase in association with native arsenic, arsenolite,chongite, talmessite and torrecillasite. Gajardoite occurs as hexagonal plates up to ∼100 μm in diameter and 5 μm thick, in rosette-like subparallel intergrowths. Crystals are transparent, with vitreous lustre and white streak. The Mohs hardness is ∼1½, tenacity is brittleand fracture is irregular. Cleavage is perfect on {001}. The measured density is 2.64 g/cm3 and the calculated density is 2.676 g/cm3. Optically, gajardoite is uniaxial (–) with ω = 1.780(3) and ε = 1.570(5) (measured in white light). The mineral is very slowly soluble in H2O and slowly soluble in dilute HCl at room temperature. The empirical formula, determined from electron-microprobe analyses, is (K0.77Ca0.71Na0.05Mg0.05)∑1.58As4O11Cl1.96H9.62.Gajardoite is hexagonal, P6/mmm, a = 5.2558(8), c = 15.9666(18) Å, V = 381.96(13) Å3 and Z = 1. The eight strongest powder X-ray diffraction lines are [dobs Å(I)(hkl)]: 16.00(100)(001), 5.31(48)(003),3.466 (31)(103), 3.013(44)(104), 2.624(51)(006,110,111), 2.353(36)(113), 1.8647(21)(116,205) and 1.4605(17) (119,303,216). The structure, refined to R1 = 3.49% for 169 Fo > 4σF reflections, contains two types of layers. One layer of formulaKAs3+4O6Cl2 consists of two neutral As2O3 sheets, between which are K+ cations and on the outside of which are Cl– anions. This layer is topologically identical to a slice of the lucabindiite structureand similar to a slice of the torrecillasite structure. The second layer consists of an edge-sharing sheet of Ca(H2O)6 trigonal pyramids with isolated H2O groups centred in the hexagonal cavities in the sheet.

The new mineral chongite (IMA2015–039), Ca3Mg2(AsO4)2(AsO3OH)2.4H2O, was found at the Torrecillas mine, Iquique Province, Chile, where it occurs as a secondary alteration phase in association with native arsenic, arsenolite, gajardoite, talmessite and torrecillasite. Chongite occurs as prismatic crystals up to ∼1 mm long grouped in tightly intergrown radial aggregates up to 2 mm in diameter. Crystals are transparent, with vitreous lustre and white streak. The Mohs hardness is ∼3½, tenacity is brittle and fracture is conchoidal. Cleavage is good on ﹛100﹜. The measured density is 3.09(2) g/cm3 and the calculated density is 3.087 g/cm3. Optically, chongite is biaxial (-) with α = 1.612(1), β= 1.626(1), γ= 1.635(1) and 2V = 76.9(1)° (measured in white light). Dispersion is r < v, distinct. The optical orientation is X= b;Z^a = 27° in obtuse angle β. The mineral is slowly soluble in dilute HCl at room temperature. The empirical formula, determined from electron-microprobe analyses, is (Ca2.90Mg1.93Mn0.14)Σ4.97As4O20H10.07. Chongite is monoclinic, die, a = 18.5879(6), b = 9.3660(3), c = 9.9622(7) Å, β = 96.916(7)°, V= 1721.75(14) Å3 and Z=4. The eight strongest powder X-ray diffraction lines are [dobs Å(I)(hkl)]: 8.35(29)(110), 4.644(62) (3ˉ11,020,400,2̄02), 4.396(26)(311), 3.372(62)(022,312,5̄11), 3.275(100)(420,22ˉ2,421), 3.113(57)(222), 2.384(30)(711,530,7̄12) and 1.7990(22)(9̄13,334,5̄34). The structure determination (R1 = 1.56% for 1849 Fo > 4σF reflections) confirms that chongite is a member of the hureaulite group.