The ammonium acetate saturation (AMAS) method was used to study the cation-exchange capacity (CEC) of zeolitic volcaniclastic materials from Santorini and Polyegos Islands, Greece. The AMAS method was tested with respect to the time required to saturate the samples of zeolites with ammonium (NH4+) ions, the efficient liberation of NH4+ ions, and the suitability of two widely used techniques to measure ammonia (NH3) (Kjeldahl ammonia distillation technique and the ammonia electrode technique). By using the inductively coupled plasma-mass spectrometry (ICP-MS) technique and measuring the number of cations exchanged during ammonium acetate (NH4OAc) saturation, it was found that the saturation period for zeolitic materials must be increased to 12-day cycles to ensure effective saturation. Following NH4OAc saturation, the AMAS method produces NH4+ solutions, after the NH4+-saturated samples of zeolites are washed with 10% NaCl. The amount of the NH4+ ions in solution (i.e., exchangeable cations) is a measure of the CEC. The NH4+ ions can not be directly measured and must be converted to NH3. The Kjeldahl ammonia distillation technique and the ammonia electrode technique for measuring NH3 give identical CEC results. However, the ammonia electrode technique, when used directly with the NH4+ samples of zeolite without 10% NaCl treatment, generally gives higher CEC values. The amount of NH4+ treated (converted to NH3), when the NH4+-saturated zeolitized samples were used directly, was higher than the amount of the NH4+ treated when the NH4+ solutions were obtained after washing the NH4+-saturated zeolitized samples with 10% NaCl. Therefore, washing with 10% NaCl does not facilitate the release of all NH4+ initially within the zeolite structure. A modified AMAS technique is proposed for measuring the CEC of zeolitic material.

The vitric component of the silicic pyroclastic flows and surge deposits (Prassa ignimbrite unit), from the northwestern exposures of the pyroclastics formation of Polyegos Island, South Aegean Sea Volcanic Arc in Greece, is replaced by authigenic zeolite and clay minerals. Mordenite dominates, and clinoptilolite (heulandite type 3), illite and illite-smectite (I-S) are subordinate. Opal-CT, quartz, feldspar, biotite and halite complete the mineralogical suite. In the southwestern part of the pyroclastics formation (Myrsini pyroclastics unit), kaolinite, halloysite, alunite and amorphous silica are the major mineralogical constituents as a result of a strong hydrothermal alteration by solutions enriched in SO42-. Scanning electron microscope (SEM) examination proved that the 1st type of zeolites formed within the area were heulandite minerals, following the formation of smectite, as a result of the activity of pore fluids within the volcaniclastic pile. There was no substantial evidence to support a hypothesis that mordenite was formed with the heulandite minerals after the initial stages of glass dissolution, other than some very minor mordenite that was formed from a gel-like type of material. The majority of mordenite present is most often draped over and formed from the crystals of heulandite minerals. Heulandite minerals often show advanced dissolution effects. The mineral dissolution was due to the emplacement of rhyolite lava domes and flows and the associated temperature rise and circulation of hydrothermal fluids, which had also mixed with seawater. The volcanic activity raised the temperature and changed the pore fluid chemistry, and the more unstable members of the heulandite minerals group were transformed to mordenite. Clinoptilolite (heulandite type 3), which was found within a few samples, was thermally more stable than any heulandite type 1 or 2 phases initially present. Therefore, clinoptilolite was either transformed more slowly or within a very few cases, it has not been affected at all. A heulandite-minerals-derived material acted as the major precursor for the formation of mordenite. The temperature increase within the area and the later hydrothermal alteration effect are also indicated by the illitization of the smectite. Mordenite is also found to have formed from I-S clays. Overall, mordenite formed as a result of elevated temperature and high Na+ concentration.