Pillared structures with an interlayer opening of ∼0.3 nm were obtained after successive heat treatments of the PILC precursor in reducing and oxidizing conditions. This precursor was prepared by reacting a Na+-montmorillonite with an intercalant containing Al and Fe oxo-hydroxides (Al/Fe = 1). Powder X-ray diffraction, elemental analysis, 57Fe Mössbauer spectroscopy, catalytic activity measurements and surface area data were used to characterize the samples. On the basis of Mössbauer spectra taken at temperatures between 4.2 and 300 K, it is deduced that oxidizing steps produce Al substituted maghemite which converts into Al substituted magnetite upon reducing heat treatment. Firing the precursor in oxidizing atmosphere forms pillars of few nm in diameter. However, heating under reducing conditions yields pillars of smaller diameter. This later behaviour is maintained even after reheating the material in oxidizing atmosphere. From the temperature dependence of Mössbauer spectra it is deduced that the diameter of the Fe oxide particles in the pillars is smaller than 10 nm.

Two novel adsorbents – montmorillonite (Mnt)-hyamine and Mnt-hyamine-sodium dodecyl sulfate (SDS) – were synthesized using Mnt nanoparticles. The modified Mnt and Mnt nanoparticles were used for the removal of crystal violet from water, and they were characterized using various techniques. The effects of pH, time, temperature, adsorbent dosage and initial dye concentration on the dye-removal efficiency were investigated using response surface methodology. The optimum conditions for maximum dye removal were obtained. The optimum conditions for crystal violet adsorption on Mnt-hyamine, Mnt-hyamine-SDS and Mnt nanoparticles are temperatures 25.00°C, 29.97°C and 27.28°C; pH values 9.00, 10.41 and 9.40; adsorbent dosages 1.00, 1.15 and 1.06 g L–1; and initial dye concentrations 30.00, 98.74 and 99.44 mg L–1, respectively. The adsorbent dosage is the most critical variable for dye removal. Temkin and Langmuir are the best isotherms for studying adsorption equilibria. In the kinetic study, the fractal-like integrated kinetic Langmuir model was the most appropriate model, and the thermodynamic parameters were also determined. The synthesized adsorbents could be easily separated from solution. The Mnt-hyamine-SDS adsorbent has a high adsorption capacity (690.69 mg g–1) for the removal of crystal violet.