Neutron Irradiated Uranium Silicides Studied by Neutron Diffraction and Rietveld Analysis

Published online by Cambridge University Press:  21 February 2011

R. C. Birtcher
Affiliation:
Argonne National Laboratory, Argonne, IL 60439
M. H. Mueller
Affiliation:
Argonne National Laboratory, Argonne, IL 60439
J. W. Richardson Jr.
Affiliation:
AMOCO Research Center, P.O. Box 3011, Naperville, IL 60566
J. Faber Jr.
Affiliation:
AMOCO Research Center, P.O. Box 3011, Naperville, IL 60566
Get access

Extract

Uranium silicides have been considered for use as reactor fuels in both high power and low enrichment applications. However, U3 Si was found to become amorphous under irradiation [1] and to become mechanically unstable to rapid growth by plastic flow [2,3]. U3Si2 appears to be stable against amorphization at low displacement rates, but the extent of this stability is uncertain. Although the mechanisms responsible for plastic flow in U3Si and other amorphous systems are unknown, as is the importance of crystal structure for amorphization, it may not be surprising that these materials amorphize, in light of the fact that many radioactive nuclide - containing minerals are known to metaminctize (lose crystallinity) under irradiation [4]. The present experiment follows the detailed changes in the crystal structures of U3Si and U3Si2 introduced by neutron bombardment and subsequent uranium fission at room temperature. U-Si seems the ideal system for a neutron diffraction investigation- since the crystallographic and amorphous forms can be studied simultaneously by combining conventional Rietveld refinement of the crystallographic phases with Fourier-filtering analysis [5] of the non-crystalline scattering component.

Type
Research Article
Copyright
Copyright © Materials Research Society 1990

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

[1] Walker, D. G., J. Nucl. Mat. 37, 48 1970).Google Scholar
[2] Hofman, G. L., J. Nucl. Mat. 140, 256 (1986).Google Scholar
[3] Birtcher, R. C., Allen, C. W., Rehn, L. E. and Hofman, G. L., J. Nucl. Mater. 152, 73 (1988).Google Scholar
[4] Bayless, P., Mazzi, F., Munno, R. and White, T. J., Mineral. Mag. 53, 565 (1989).Google Scholar
[5] Richardson, J. W. Jr., and Faber, J. Jr., Adv. X-ray anal. 29, 143 (1985).Google Scholar
[6] Birtcher, R. C., Blewitt, T. H., Kirk, M. A., Scott, T. L., Brown, B. S. and Greenwood, L. R., J. Nucl. Mater. 108 & 109, 3 (1982).Google Scholar
[7] Greenwood, L. R., private communication.Google Scholar
[8] Parkin, D. M. and Elliott, R. O., Nucl. Inst. Meth. B16, 193 (1986).Google Scholar
[9] Rietveld, H. M., J. Appl. Cryst. 2, 65 (1969).Google Scholar
[10] Jorgensen, J. D., Faber, J. Jr., Carpenter, J. M., Crawford, R. K., Hauman, J. R., Hitterman, R. L., Kleb, R., Ostrowski, G. E., Rotella, F. J. and Worlton, T. G., J. Appl. Cryst. 21, 321 (1989).Google Scholar
[11] Zachariasen, W. H., Acta Cryst. 2, 94 (1949).Google Scholar
[12] Kimmel, G. and Nadiv, S., Acta Cryst. B31, 1351 (1975).Google Scholar
[13] Blum, P. L., Silvestro, G. and Vangoyan, H., C. R. Acad. Sci. 260, 5538 (1964).Google Scholar