Magnetic Domains in Epitaxial (100) Fe Thin Films

Published online by Cambridge University Press:  03 September 2012

Jeffrey M. Florczak ,
P. J. Ryan ,
J. N. Kuznia ,
A. M. Wowchak ,
P. I. Cohen ,
R. M. White ,
G. A. Prinz  and
E. Dan Dahlberg
Jeffrey M. Florczak
Affiliation:
School of Physics and Astronomy, University of Minnesota, Minneapolis, MN 55455
P. J. Ryan
Affiliation:
Control Data Corp., 8100 34th. Ave. S., Mpls., MN 55440
J. N. Kuznia
Affiliation:
Department of Electrical Engineering, University of Minnesota, Minneapolis, MN 55455
A. M. Wowchak
Affiliation:
Department of Electrical Engineering, University of Minnesota, Minneapolis, MN 55455
P. I. Cohen
Affiliation:
Department of Electrical Engineering, University of Minnesota, Minneapolis, MN 55455
R. M. White
Affiliation:
Control Data Corp., 8100 34th. Ave. S., Mpls., MN 55440
G. A. Prinz
Affiliation:
Naval Research Laboratory, Washington, D.C. 20375-5000
E. Dan Dahlberg
Affiliation:
School of Physics and Astronomy, University of Minnesota, Minneapolis, MN 55455
Get access

Abstract

By use of Kerr microscopy, the domain patterns of thin Fe films (10 nm) grown on Inx Ga1-x As (0.09 ≤ x ≤ 0.25)/GaAs substrates have been investigated. For This nvestigation, two types of InGaAs buffer layers were prepared. One consisted of a single, thick InGaAs layer and the second composed of an InGaAs strained layer superlattice. Both were grown on (100) GaAs substrates. The study showed that many of the domain walls were approximately parallel to the easy axis of Fe for those films grown on the low x alloy, e.g. x-0.1, InGaAs buffer layers. In the alloy films with larger values of x, e.g. x-0.2, the domain pattern of the Fe overlayer was strongly influenced by dislocations of the strain relieved InGaAs buffer layer. These dislocations manifested themselves as corrugations parallel to the <110> directions in the InGaAs. Kerr microscopy of a x-0.2 film indicated the presence of long, narrow domains with their long axes parallel to the striations. Although shape anisotropy arguments predicted that the magnetization should be parallel to the striations, magnetometer data indicated that a substantial component of magnetization was oriented perpendicular to the corrugations at low fields. The Fe film grown on the superlattice had magnetic domains very similar to a thick Fe film (0.5 μm) grown on GaAs.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 151: Symposium G – Growth, Characterization and Properties of Ultrathin Magnetic Films and Multilayers , 1989 , 213
Copyright
Copyright © Materials Research Society 1989

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

[1] Fu, C.L., Freeman, A.J., and Oguchi, T., Phys. Rev. Lett. 54 2700 (1985)Google Scholar
[2] Jonker, B.T., Walker, K.H., Kisker, E., Prinz, G.A., and Carbone, C., Phys. Rev. Lett. 57 142 (1986)Google Scholar
[3] Baibich, M.N., Broto, J.M., Fert, A., Dau, F. Nguyen Van, Petroff, F., Eitenne, P., Creuzet, G., Friederich, A., and Chazelas, J., Phys. Rev. Lett. 61, 2472 (1988)Google Scholar
[4] Araya-Pochet, J., Ballentine, C.A., and Erskine, J. L., Phys. Rev. B 38, 7846 (1988)Google Scholar
[5] Kavanagh, K.L., Capone, M.A., Hobbs, L.W., Barbour, L.C., Maree, P.M.J., Schaff, W., Mayer, J.W., Pettit, D., Woodall, J.M., Stroscio, J.A., and Feenstra, R.M., J. Appl. Phys. 64, 4843 (1988)Google Scholar
[6] Krebs, J.J., Rachford, F.J., Lubitz, P., and Prinz, G.A., J. Appl. Phys. 53, 8058 (1982)Google Scholar
[7] Florczak, J.M. and Dahlberg, E. Dan, to be submitted for publication.Google Scholar