Fabrication of Improved p-AgGaSe2/n-Si Heterojunction Solar Cells on Optimum Quality Thermally Evaporated AgGaSe2 Thin Films

Published online by Cambridge University Press:  28 June 2011

Sandip Das  and
Krishna C. Mandal
Sandip Das
Affiliation:
Department of Electrical Engineering, University of South Carolina, Columbia, SC 29208, USA
Krishna C. Mandal
Affiliation:
Department of Electrical Engineering, University of South Carolina, Columbia, SC 29208, USA
Get access

Abstract

Optimum quality polycrystalline AgGaSe2 thin films were deposited on H-terminated n-Si substrates by controlled thermal evaporation method. The film deposition conditions were varied to optimize the structure and optoelectronic properties of AgGaSe2 thin films. X-ray diffraction (XRD) studies showed that all AgGaSe2 films were of chalcopyrite structure and while the films deposited at room temperature (300 K) had random grain orientation, the films deposited at higher substrate temperature (≥ 450K) showed preferred (112) orientation. The composition of the films were analyzed by electron probe microanalysis (EPMA) deposited at different substrate temperatures. The ultraviolet-visible (UV-Vis) spectra showed the optical bandgap of 1.80 eV, with sharper band edge for the films deposited at higher temperature. The films were p-type and the resistivities of the as deposited films at 300 and 650K were ~5×103 and ~200 Ω.cm respectively. p-AgGaSe2/n-Si heterojunction solar cells, having an active area of 0.18 cm2 without any antireflection coating were designed and fabricated. It was observed that the films deposited at 650K produced heterojunctions with significantly improved photovoltaic properties. The evidence of the barrier height modifications have been provided by C-V measurements. Under solar simulator AM1 illumination, the improved junction exhibited an efficiency of 5.2%, whereas the AgGaSe2 films deposited at 300K showed a lower efficiency of 2.1%.

Keywords

photovoltaicthin filmcrystalline
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1323: Symposium C – Advanced Materials Processing for Scalable Solar-Cell Manufacturing , 2011 , mrss11-1323-c03-11
Copyright
Copyright © Materials Research Society 2011

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Route, R.K., Feigelson, R.S. and Raymakers, R.J., J. Cryst. Growth, 24/25, 390 (1974).Google Scholar
2. Eckardt, R.C., Fan, Y.X., Byer, R.L., Marquardt, C.L., Strom, M.E., and Esterowitz, L., Appl. Phys. Lett., 49, 608 (1986).Google Scholar
3. Byer, R.L., Choy, M.M., Herbst, R.L., Chemla, D.S., and Fiegelson, R.S., Appl. Phys. Lett., 24, 65 (1974).Google Scholar
4. Bianchi, A. and Garby, M., Opt. Commun., 30, 122 (1979).Google Scholar
5. Roy, U.N., Cui, Y., Miles, R., Burger, A., Goldstein, J.T., Bell, Z.W., and Carpenter, D.A., J. Appl. Phys., 98, 93523 (2005).Google Scholar
6. Brisson, O., El Ganaoui, M., Simonnet, A., and Launay, J.C., J. Crystal Growth, 204 (1999) 201.Google Scholar
7. Hahn, S.-R., Kim, W.-T., Kim, Y.-G., J. Appl. Phys., 69, 7797 (1991).Google Scholar
8. Satyanarayana Murty, Y., Mahammad Hussain, O., Srinivasulu Naidu, B., and Jayarama Reddy, P., Mater. Lett., 10, 504 (1987).Google Scholar
9. Roy, U.N., Groza, M., Cui, Y., Burger, A., Bell, Z.W., and Carpenter, D.A., Proc. SPIE, 177, 5540 (2004).Google Scholar
10. Melloch, M.R., Harmon, E.S., and Emery, K.A., IEEE Electron Device Lett., 12, 137 (1991).Google Scholar
11. Tompa, G.S., Nelson, C.R., Sarcacino, M.A., Colter, P.C., Anderson, P.L., Wright, W.H., and Schimdt, J.L., Appl. Phys. Lett., 55, 62 (1989).Google Scholar
12. Savadogo, O. and Mandal, K.C., J. Phys. D: Appl. Phys., 27, 1070 (1997).Google Scholar
13. Das, S.R., Banerjee, A., and Chopra, K.L., Solid State Electron., 22, 65 (1987).Google Scholar
14. Mandal, K.C., Ozanam, F., and Chazalviel, J.-N., Appl. Phys. Lett., 57, 2788 (1990).Google Scholar
15. Mandal, K., Ozanam, F., Chazalviel, J.-N., J. Electroanal. Chem., 336, 153 (1992).Google Scholar
16. Vincett, P.S., Barlow, W.A., and Roberts, G.G., J. Appl. Phys., 48, 3800 (1977).Google Scholar