Effects of N2O Fluence on the PECVD-grown Si-rich SiOx with Buried Si Nanocrystals

Published online by Cambridge University Press:  01 February 2011

Chun-Jung Lin ,
Hao-Chung Kuo ,
Chia-Yang Chen ,
Yu-Lun Chueh ,
Li-Jen Chou ,
Chih-Wei Chang ,
Eric Wei-Guang Diau  and
Gong-Ru Lin
Chun-Jung Lin
Affiliation:
Department of Photonics and Institute of Electro-Optical Engineering National Chiao Tung University, 1001 Ta Hsueh Road, Hsinchu, Taiwan 300, R.O.C.
Hao-Chung Kuo
Affiliation:
Department of Photonics and Institute of Electro-Optical Engineering National Chiao Tung University, 1001 Ta Hsueh Road, Hsinchu, Taiwan 300, R.O.C.
Chia-Yang Chen
Affiliation:
Department of Photonics and Institute of Electro-Optical Engineering National Chiao Tung University, 1001 Ta Hsueh Road, Hsinchu, Taiwan 300, R.O.C.
Yu-Lun Chueh
Affiliation:
Department of Materials Science and Engineering National Tsing Hua University, 101, Section 2 Kuang Fu Road, Hsinchu, Taiwan 300, R. O. C.
Li-Jen Chou
Affiliation:
Department of Materials Science and Engineering National Tsing Hua University, 101, Section 2 Kuang Fu Road, Hsinchu, Taiwan 300, R. O. C.
Chih-Wei Chang
Affiliation:
Department of Applied Chemistry and Center for Interdisciplinary Molecular Science National Chiao Tung University, 1001 Ta Hsueh Road, Hsinchu, Taiwan 300, R.O.C.
Eric Wei-Guang Diau
Affiliation:
Department of Applied Chemistry and Center for Interdisciplinary Molecular Science National Chiao Tung University, 1001 Ta Hsueh Road, Hsinchu, Taiwan 300, R.O.C.
Get access

Abstract

The optimized N2O fluence is demonstrated for plasma enhanced chemical vapor deposition (PECVD) of Si-rich substoichiometric silicon oxide (SiOx) films with buried Si nanocrystals. Strong room-temperature photoluminescence (PL) at 550-870 nm has been observed in SiOx films grown by PECVD under a constant SiH4 fluence of 20 sccm with an N2O fluence varying from 105 sccm to 130 sccm. A 22-nm-redshift in the central PL wavelength has been detected after annealing from 15 min to 180 min. The maximum PL irradiance is observed from the SiOx film grown at the optimal N2O fluence of 120 sccm after annealing for 30 minutes. Larger N2O fluence or longer annealing time leads to a PL band that is blue-shifted by 65 nm and 20 nm, respectively. Such a blue shift is attributed to shrinkage in the size of the Si nanocrystals with the participation of oxygen atoms from N2O incorporated within the SiOx matrix. The (220)-oriented Si nanocrystals exhibit radii ranging from 4.4 nm to 5.0 nm as determined by transmission electron microscopy (TEM). The luminescent lifetime lengthens to 52 μs as the nc-Si size increase to > 4 nm. Optimal annealing times for SiOx films prepared at different N2O fluences are also reported. A longer annealing process results in a stronger oxidation effect in SiOx films prepared at higher N2O fluences, yielding a lower PL irradiance at shorter wavelengths. In contrast, larger Si nanocrystals can be precipitated when the N2O fluence becomes lower; however, such a SiOx film usually exhibits weaker PL at longer wavelength due to a lower nc-Si density. These results indicate that a N2O/SiH4 fluence ratio of 6:1 is the optimized PECVD growth condition for the Si-rich SiO2 wherein dense Si nanocrystals are obtained after annealing.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 862: Symposium A – Amorphous and Nanocrystalline Silicon Science and Technology–2005 , 2005 , A19.11
Copyright
Copyright © Materials Research Society 2005

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Song, F. Z., and Bao, X. M., Phys. Rev. B 55, 6988 (1997).10.1103/PhysRevB.55.6988Google Scholar
2 Delerue, C., Allan, G., and Lannoo, M., Phys. Rev. B 48, 11024 (1993).10.1103/PhysRevB.48.11024Google Scholar
3 Iacona, F., Franzò, G., and Spinella, C., J. Appl. Phys. 87, 1295 (2000).10.1063/1.372013Google Scholar
4 Verdeyen, J. T., Laser Electronics (Englewood Cliffs, NJ: Prentice Hall, 1995) pp. 179–182.Google Scholar
5 Kovalev, D., Diener, J., Heckler, H., Polisski, G., Kunzner, N., and Koch, F., Phys. Rev. B 61, 4485 (2000).10.1103/PhysRevB.61.4485Google Scholar
6 Garcia, C., Garrido, B., Pellegrino, P., Ferre, R., Moreno, J. A., Morante, J. R., Pavesi, L., and Cazzanelli, M., Appl. Phys. Lett. 82, 1595 (2003).10.1063/1.1558894Google Scholar
7 Lopez, M., Garrido, B., Garcia, C., Pellegrino, P., Perez-Rodriguez, A., Morante, J. R., Bonafos, C., Carrada, M., and Claverie, A., Appl. Phys. Lett. 80, 1637 (2002).10.1063/1.1456970Google Scholar
8 Madelung, O., Introduction to Solid State Theory (Berlin: Springer-Verlag, 1978) Ch. 6.10.1007/978-3-642-61885-7Google Scholar
9 Donati, S., Photodetectors Devices, Circuits, and Applications (Upper Saddle River, NJ: Prentice Hall, 2000) p 11.Google Scholar
10 Pacifici, D., Moreira, E. C., Franzò, G., Martorino, V., Priolo, F., and Iacona, F., Phys. Rev. B 65, 144109 (2002).10.1103/PhysRevB.65.144109Google Scholar
11 Priolo, F., Franzò, G., Pacifici, D., Vinciguerra, V., Iacona, F., and Irrera, A., J. Appl. Phys. 89, 264 (2001).10.1063/1.1331074Google Scholar
12 Bae, H. S., Kim, T. G., Whang, C. N., Im, S., Yun, J. S., and Song, J. H., J. Appl. Phys. 91, 4078 (2002).10.1063/1.1452768Google Scholar
13 Nishikawa, H., Shiroyama, T., Nakamura, R., Ohki, Y., Nagasawa, K., and Hama, Y., Phys. Rev. B 45, 586 (1992).10.1103/PhysRevB.45.586Google Scholar
14 Augustine, B. H., Irene, E. A., He, Y. J., Price, K. J., McNeil, L. E., Christensen, K. N., and Maher, D. M., J. Appl. Phys. 78, 4020 (2000).10.1063/1.359925Google Scholar