Deformation Mechanisms in Ferritic/martensitic Steels Irradiated in HFIR

Published online by Cambridge University Press:  21 March 2011

Naoyuki Hashimoto ,
Steven J. Zinkle ,
Ronald L. Klueh ,
Arthur F. Rowcliffe  and
Kiyoyuki Shiba
Naoyuki Hashimoto
Affiliation:
Oak Ridge National Laboratory, P. O. Box 2008, Oak Ridge, TN 37831-6151, USA
Steven J. Zinkle
Affiliation:
Oak Ridge National Laboratory, P. O. Box 2008, Oak Ridge, TN 37831-6151, USA
Ronald L. Klueh
Affiliation:
Oak Ridge National Laboratory, P. O. Box 2008, Oak Ridge, TN 37831-6151, USA
Arthur F. Rowcliffe
Affiliation:
Oak Ridge National Laboratory, P. O. Box 2008, Oak Ridge, TN 37831-6151, USA
Kiyoyuki Shiba
Affiliation:
Japan Atomic Energy Research Institute, Tokai, Ibaraki, 319-1195, Japan
Get access

Abstract

A reduced activation ferritic/martensitic steel, F82H (IEA heat), developed for fusion energy applications was irradiated at 300 and 500°C to 5 dpa in the High Flux Isotope Reactor (HFIR). Changes in yield strength, deformation mode, and strain-hardening capacity were seen, with the magnitude of the changes dependent on irradiation temperature. Irradiation at 300°C led to a significant loss of strain-hardening capacity with a large change in yield strength. There was a tendency for a reduction in strain rate to cause a decrease in yield strength and elongation. Irradiation at 500°C had little effect on strength, but a reduction in strain rate caused a decrease in ductility. In order to determine the contributions of different microstructural features to strength and to deformation mode, transmission electron microscopy (TEM) specimens were prepared from the gage sections of the tested (strained) flat tensile specimens and examined; fracture surfaces were examined by scanning electron microscopy (SEM). The fracture surfaces showed a martensitic mixed quasi-cleavage and ductile-dimple fracture in the center at both irradiation temperatures. The microstructure in the necked region irradiated at 300°C showed defect free bands, which may be dislocation channels. This suggests that dislocation channeling could be the dominant deformation mechanism in martensitic steels irradiated at 300°C, resulting in the loss of strain-hardening capacity.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 650: Symposium R – Microstructural Processes in Irradiated Materials-2000 , 2000 , R1.10
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Shiba, K., Proc. of the IEA Working Group Meeting on Ferritic/Martensitic Steels, September 19-20, 1995, Barden, Switzerland, ORNL/M-4939 (1995).Google Scholar
2. Pawel, J.E., Lenox, K.E., and Ioka, I., Fusion materials semiannual progress report, DOE/ER- 0313/19, 312 (1995).Google Scholar
3. Pawel, J.E., Lenox, K.E., Ioka, I., and Wakai, E., Fusion materials semiannual progress report, DOE/ER-0313/21, 249 (1996).Google Scholar
4. Grossbeck, M.L., Lenox, K.E., Janney, M.A., Muroga, T., Heatherly, W.W., and Thoms, K.R., Fusion materials semiannual progress report, DOE/ER-0313/22, 254 (1997).Google Scholar
5. Lenox, K.E. and Grossbeck, M.L., Fusion materials semiannual progress report, DOE/ER- 0313/25, 307 (1998).Google Scholar
6. Shiba, K., Klueh, R.L., Miwa, Y., Igawa, N., and Robertson, J.P., Fusion materials semiannual progress report, DOE/ER-0313/28, 131 (2000).Google Scholar
7. Haasen, P., Physical Metallurgy, Cambridge Univ. Press, New York, 1978, pp. 26.Google Scholar
8. Späig, P., Odette, G.R., and Lucas, G.E., J. Nucl. Mater. 283, 721 (2000).Google Scholar
9. Koppenaal, T.J. and Arsenault, R.J., Metall. Reviews 16, 175 (1971).Google Scholar
10. Kocks, U.F., Metall. Trans. 1, 1121 (1970).Google Scholar
11. Kelly, P.M., Int. Metal. Rev. 18, 31 (1973).Google Scholar
12. Asaro, R.J., Advances in Applied Mechanics, vol. 23, Academic Press, New York, 1993, pp.1.Google Scholar