Synthesis of Epoxy and Block Oligomer Modified Clay Nanocomposite

Published online by Cambridge University Press:  15 March 2011

Kang Hung Chen
Affiliation:
Department of Chemical and Material Engineering, National Central University, Chung-Li, Taiwan 320.
Sze Ming Yang*
Affiliation:
Department of Chemical and Material Engineering, National Central University, Chung-Li, Taiwan 320.
*
To whom all correspondence should be addressed
Get access

Abstract

Acrylic triblock (AxMyBz) and diblock (MyBz) oligomers containing methyl methacrylate (MMA, M), methacrylic acid (MAA, A) and dimethylaminoethyl methacrylate (DMAEMA, B) groups are intercalated into the layers of montmorillonite. The results indicate that the block oligomer lay flatly between the clay layers. ICP analyses of Na+ content indicate no unexchanged sodium ions are left in the intercalated clay.

Nanocomposites of epoxy and clay modified with block oligomers were synthesized. Glass transition temperature (Tg) of the nanocomposite is 129.6°C (M18B2424+ modified clay) compared to 84.1°C for the physical mixture of epoxy and unmodified clay. Tg increases with decreasing amount of modified clay. When modified clay content are below 2 phr, Tg higher than 131.7 °C can be obtained. Water resistance and light transmittance of the nanocomposite is also improved over composite of epoxy and unmodified clay.

Type
Research Article
Copyright
Copyright © Materials Research Society 2002

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Vaia, R. A., Ishii, H. and Giannelis, E. P., Chem. Mater. 5, 1694 (1993).Google Scholar
2. Messersmith, P. B. and Giannelis, E. P., Chem. Mater. 6, 1719 (1994).Google Scholar
3. Lan, T. and Pinnavaia, T. J., Chem. Mater. 6, 2216 (1994).Google Scholar
4. Lan, T., Kaviratna, D. and Pinnavaia, T. J., J. Phys. Chem. Solids. 57, 1005 (1996).Google Scholar
5. Capkova, P., Driessen, R. A. J., Numan, M., Schenk, H., Weiss, Z. and Klika, Z., Chem PapChem Zvesti 52, 1 (1998).Google Scholar
6. Chen, H. L., Wang, S. F. and Lin, T. L., Macromolecules 31, 8924 (1998).Google Scholar
7. Tsao, C. S., Lin, T. L. and Yu, M. S., Physica B 271, 322 (1999).Google Scholar
8. Patrickios, C. S., PhD. Thesis, Massachusetts Institute of Technology, 1994.Google Scholar