Silver Metallization with Reactively Sputtered TiN Diffusion Barrier Films
Published online by Cambridge University Press: 17 March 2011
Abstract
The physical and electrical properties as well as thermal stability of reactively sputtered titanium nitride (TiN) film serving as a diffusion barrier was studied for silver (Ag) metallization. The thermal stability of Ag/TiN metallizations on Si with 12-nm-thick TiN barriers, as-deposited and after annealing at 300-650°C in N2/H2 for 30 min, was investigated with sheet resistance measurement, X-ray diffraction, focused ion beam-scanning electron microscopy, atomic force microscopy and X-ray photoelectron spectroscopy. According to electrical measurement no change of sheet resistance was found after annealing at 600°C, but an abrupt rise appeared at 650°C annealing. There are two causes by which the Ag/TiN/Si structure became degraded. One is agglomeration of the silver layer, and the other is oxidation and diffusion which are also associated problems during thermal annealing.
- Type
- Research Article
- Information
- Copyright
- Copyright © Materials Research Society 2004
References
- 3
- Cited by