A Method for Producing Site-Specific TEM Specimens from Low Contrast Materials with Nanometer Precision

Published online by Cambridge University Press:  04 February 2013

Henrik Pettersson ,
Samira Nik ,
Jonathan Weidow  and
Eva Olsson
Henrik Pettersson
Affiliation:
Microscopy and Microanalysis, Department of Applied Physics, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden
Samira Nik
Affiliation:
Microscopy and Microanalysis, Department of Applied Physics, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden
Jonathan Weidow
Affiliation:
Microscopy and Microanalysis, Department of Applied Physics, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden
Eva Olsson*
Affiliation:
Microscopy and Microanalysis, Department of Applied Physics, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden
*
*Corresponding author. E-mail: [email protected]
Get access

Abstract

A method that enables high precision extraction of transmission electron microscope (TEM) specimens in low contrast materials has been developed. The main idea behind this work is to produce high contrast markers on both sides of and close to the area of interest. The markers are filled during the depositing of the protective layer. The marker material can be of either Pt or C depending on which one gives the highest contrast. It is thereby possible to distinguish the location of the area of interest during focused ion beam (FIB) milling and ensure that the TEM sample is extracted precisely at the desired position. This method is generally applicable and enables FIB/scanning electron microscope users to make high quality TEM specimens from small features and low contrast materials without a need for special holders. We explain the details of this method and illustrate its potential by examples from three different types of materials.

Keywords

specimen preparationlow-contrast materialssite-specificscanning electron microscopyfocused ion beamlift-outtransmission electron microscopy
Type
Software, Techniques and Equipment Development
Information
Microscopy and Microanalysis , Volume 19 , Issue 1 , February 2013 , pp. 73 - 78
Copyright
Copyright © Microscopy Society of America 2013

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Amin, M.H.S., Smirnov, A.Y., Zagoskin, A.M., Lindström, T., Charlebois, S.A., Claeson, T. & Tzalenchuk, A.Y. (2005). Silent phase qubit based on d-wave josephson junctions. Phys Rev B 71, 064516. Google Scholar
Bals, S., Tirry, W., Geurts, R., Yang, Z. & Schryvers, D. (2007). High-quality sample preparation by low kV FIB thinning for analytical TEM measurements. Microsc Microanal 13, 80–86.Google Scholar
Dai, J.Y., Tee, S.F., Tay, C.L., Song, Z.G., Ansari, S., Er, E. & Redkar, S. (2001). Development of a rapid and automated TEM sample preparation method in semiconductor failure analysis and the study of the relevant TEM artifact. Microelec J 32, 221–226.Google Scholar
Edwards, H.K., Coe, S.C., Fay, M.W., Scotchford, C.A., Grant, D.M. & Brown, P.D. (2008). Site-specific, cross-sectional imaging of biomaterials and the cell/biomaterial interface using focused ion beam/scanning electron microscopy. J Phys Conf Ser 126, 012097. Google Scholar
Exner, H.E. (1979). Physical and chemical nature of cemented carbides. Int Met Rev 4, 149–173.Google Scholar
Felfer, P., Ringer, S.P. & Cairney, J.M. (2011). Shaping the lens of the atom probe: Fabrication of site specific, oriented specimens and application to grain boundary analysis. Ultramicroscopy 111, 435–439.Google Scholar
Floresca, H.C., Jeon, J., Wang, J.G. & Kim, M.J. (2009). The focused ion beam fold-out: Sample preparation method for transmission electron microscopy. Microsc Microanal 15, 558–563.Google Scholar
Giannuzzi, L.A. & Stevie, F.A. (1999). A review of focused ion beam milling techniques for TEM specimen preparation. Micron 30, 197–204.Google Scholar
Heaney, P.J., Vicenzi, E.P., Giannuzzi, L.A. & Livi, K.J.T. (2001). Focused ion beam milling: A method of site-specific sample extraction for microanalysis of earth and planetary materials. Am Mineral 86, 1094–1099.Google Scholar
Hilgenkamp, H. & Mannhart, J. (2002). Grain boundaries in high-T c superconductors. Rev Mod Phys 74, 485–549.Google Scholar
Jordan, J., Moore, M. & Young, R. (2002). Omniprobe technical note. Hillsboro, OR: FEI Company. Google Scholar
Kamino, T., Yaguchi, T., Hashimoto, T., Ohnishi, T. & Umemura, K. (2005). FIB micro-sampling technique and a site specific TEM specimen preparation method. In Introduction to Focused Ion Beams, Instrumentation, Theory, Technique and Practice, Giannuzzi, L.A. & Stevie, F.A. (Eds.), pp. 229–245. New York: Springer Science+Business Media, Inc. Google Scholar
Ke, X., Bals, S., Negreira, A.R., Hantschel, T., Bender, H. & van Tendeloo, G. (2009). TEM Sample preparation by FIB for carbon nanotube interconnects. Ultramicroscopy 109, 1353–1359.Google Scholar
Langford, R.M. & Petford-Long, A.K. (2001). Preparation of transmission electron microscopy cross-section specimens using focused ion beam milling. J Vac Sci Technol A 19, 2186. Google Scholar
Lawrence, P. (2006). The Dualbeam (FIB/SEM) and its applications—Nanoscale sample preparation and modification. Singapore: PTE Ltd Pacific Tech Centre. Google Scholar
Li, J., Malis, T. & Dionne, S. (2006). Recent advances in FIB-TEM specimen preparation techniques. Mater Charact 57, 64–70.Google Scholar
Mitsuishi, K., Shimojo, M., Tanaka, M., Takeguchi, M., Song, M. & Furuya, K. (2006). TEM sample preparation using a new nanofabrication technique combining electron-beam-induced deposition and low-energy ion milling. Microsc Microanal 12, 545–548.Google Scholar
Reyntjens, S. & Puers, R. (2001). A review of focused ion beam applications in microsystem technology. J Micromech Microeng 11, 287–300.Google Scholar
Schwarz, S.M. & Giannuzzi, L.A. (2004). FIB specimen preparation for STEM and EFTEM tomography. Microsc Microanal 10(Suppl 2), 142–143.Google Scholar
Stevie, F.A., Vartuli, C.B., Giannuzzi, L.A., Shofner, T.L., Brown, S.R., Rossie, B., Hillion, F., Mills, R.H., Antonell, M., Irwin, R.B. & Purcell, B.M. (2001). Application of focused ion beam lift-out specimen preparation to TEM, SEM, STEM, AES and SIMS analysis. Surf Interf Anal 31, 345–351.Google Scholar
Tan, E., Mather, P.G., Perrella, A.C., Read, J.C. & Buhrman, R.A. (2005). Oxygen Stoichiometry and instability in aluminum oxide tunnel barrier layers. Phys Rev B 71, 161401. Google Scholar
Unocic, K.A., Mills, M.J. & Daehn, G.S. (2008). Challenges in preparing aluminum alloys for grain boundary characterization. Microsc Microanal 14(Suppl 2), 556–557CD.Google Scholar
van Leer, B. & Giannuzzi, L.A. (2008). Advances in TEM sample preparation using a focused ion beam. Microsc Microanal 14(Suppl 2), 380–381CD.Google Scholar
Weidow, J., Norgren, S. & Andrén, H.-O. (2009). Effect of V, Cr and Mn additions on the microstructure of WC–Co. Int J Refract Met Hard Mater 27, 817–822.Google Scholar