Low Thermal Expansion of Alkali Zirconium Phosphates Using a Microcomputer Automated Diffractometer

Published online by Cambridge University Press:  06 March 2019

G. E. Lenain ,
H. A. McKinstry  and
S. Y. Limaye
G. E. Lenain
Affiliation:
Materials Research Laboratory The Pennsylvania State University University Park, PA 16802
H. A. McKinstry
Affiliation:
Materials Research Laboratory The Pennsylvania State University University Park, PA 16802
S. Y. Limaye
Affiliation:
Materials Research Laboratory The Pennsylvania State University University Park, PA 16802
Get access

Extract

The thermal expansion of ceraptic materials has become a property of interest to more people recently since the desirability of a thermally stable space platform was recognized. The interest in low thermal expansion materials in the past has been driven mildly by the recognition that low thermal expansion will foster good thermal shock resistance. The tradition of the ceramics industry for nearly one hundred years has been that zircon and cordierite were the low expanding materials. Fused silica has long been recognized for its low expansion. But when in 1947 Hummel (1957, I960) found ultra-low-expanding bodies in the lithium aluminum silicates with spodumene and later β-eucryptite structures, a new kind of phenomena had been introduced. Roy (1949), Roy, Roy and Osborn (1950) and Roy and Osborn (1959) provided much of the crystal chemical and phase diagram background on this family.

Type
X. XRD Applications
Information
Advances in X-Ray Analysis , Volume 28: Thirty-Third Annual Conference on Applications of X-ray Analysis, July 30 - August 3, 1984 , 1984 , pp. 345 - 352
Copyright
Copyright © International Centre for Diffraction Data 1984

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Alamo, J., and Roy, R., “Ultra Low Expansion Ceramics in the System Na2O-ZrO2-P2O5-SiO2 ,” Comm, J. Am. Cer. Soc. 67, C78 (1984).Google Scholar
Buesaem, W.R., and Lange, F.F., “Residual Stresses in Anisotropic Ceramics,” Interceram. 15, 229–231 (1966).Google Scholar
Cullity, B., “Elements of X-Ray Diffraction—Second Edition,” Addison-Wesley Pub. Co, Inc., Reading, MA, pp. 350–368 (1978).Google Scholar
Gillery, F.H., and Bush, E.A., “Thermal Contraction of β-Eucryptite (Li2O.Al2O2.2siO2) by X-Ray Dilatometer Methods,” J. Am. Cer. Soc. 42(4), 175–177 (1959).Google Scholar
Hagman, L., and Kierkegaard, P., “The Crystal Structure of NaMe2 IV (PO4)3; MeIV = Ge,Ti,Zr,” Act a Chem. Scan 22, 1822-1832 (1968).Google Scholar
Hong, H. Y-P., “Crystal Structures and Crystal Chemistry in the System Na1+xZr2SixP3-xO12 ,” Mat. Res. Bull. 11, 173–182 (1976).Google Scholar
Hummel, F. A., “Thermal Shock Resistant Ceramic Body,” U.S. Patent 2,785,080 (1957). (This is reissue No. 24, 795--a continuation-inpart of pending application No. 72,802 filed Jan, 26, 1949, now abandoned.)Google Scholar
Hummel, F.A., “Thermal Shock Resistant Ceramic Body,” U.S. Patent Re24,795 (1960). (This is are issue of Patent No. 2,785,080 dated March 12, 1957, Serial No. 170,426, June 23, 1950.)Google Scholar
Lenain, G.E., McKinstry, H.A., Limaye, S.Y., and Woodward, A., “Low Thermal Expansion of Alkali-Zirconium Phosphates,” Mat. Res, Bull. (1984a) (submitted for publication).Google Scholar
Lenain, G.E., McKinstry, H. A., and Limaye, S.Y., “Structural Model for Thermal Expansion in [NZP], ” J. Am. Cer. Soc. (1984b) (submitted for publication),Google Scholar
McKinstry, H.A., Shull, H. A., and Buessem, W.R., “Localized Stress in Elastic Polycrystalline Materials, ” Computer Simulation for Materials Applications,” Nucl. Metal. 20(2), 695 (1976a).Google Scholar
McKinstry, H.A., Shull, H.E., and Buessem, W. R., “Stress and Strain Fields in IdealisedGoogle Scholar
Polycrystalline Materials and the Predictions of Fracture Initiation Sites, Computer Simulation for Materials Applications,” Hucl. Metal. 20(2), 929 (1976b).Google Scholar
Megaw, H.D., “Crystal Structures: A Working Approach,” W.B. Saunders Co., Philadelphia, pp. 453–459 (1973).Google Scholar
Roy, R., “Phase Equilibria in the System Lithia-Alumina-Silica, ” Ph.D. Dissertation, The Pennsylvania State University (1949); University Microfilms, Ann Arbor, MI.Google Scholar
Roy, R., Roy, D.M., and Osborn, E. F., “Compositional and Stability Relationships Among the Lithium Aluminosilicates: Eucryptite, Spodumene, and Petalite,” J. Am. Cer. Soc. 33, 152–159 (1950).Google Scholar
Roy, R., and Osborn, E.F., “The System Lithium Metasilicate-Spodumene- Silica” J. Am. Chem, Soc. 71, 2086-2095 (1959).Google Scholar
Sljukic, M., Matkovic, B., Prodic, B., and Scavnicer, S., “Preparation and Crystallographic Data of Phosphates with Common Formula MIM2 IV(PO4)3 (MI=Li,Na,K,Rb,Cs; MIV=Zr,Hf),” Croat. Chem. Act a 39, 145–148 (1967).Google Scholar
Sljukic, M., Matkovic, B., Prodic, B., and Anderson, D., “The Crystal Structure of KZr2(PO4)3 ,” Z. Krist. 130, 148–161 (1968).Google Scholar
Smith, D.K., and Holomany, M., “A Fortran IV Program for Calculating X-Ray Powder Patterns Version 10,” Computer Science Center, The Pennsylvania State University (1983).Google Scholar