Residual strains and microstresses are evaluated for both phase of a hot-pressed, fine-grained α-alumina reinforced with 25 wt% (29 vol%) single-crystal silicon carbide whiskers at temperatures from 25 to 1000 °C. The sample was maintained in a nonoxidizing environment while measurements of the interplaner spacing of alumina (146) and SiC (511 + 333) were made using X-ray diffraction methods. The residual strains were profiled at temperature increments of 250 °C from which the corresponding microstresses were calculated. Linear extrapolation of the SiC ε33 profile indicates that the strains are completely relaxed at a temperature of approximately 1470 °C. These residual stress relaxation results suggest that elevated temperature toughness and fracture strength of this composite may result from cooperative mechanisms.