We present the results of a study of the solvothermal synthesis of mixed-metal cerium-containing oxides all prepared from CeCl3.7H2O at less than 250 ºC in single step reactions. The use of NaBiO3 in the presence of aqueous NaOH yields fluorite solid solutions Ce1-xBixO2-x/2 (x ≤ 0.6), whereas the use of either H2O2 or NaBrO3 as oxidant in the presence of TiF3 yields a Ce(IV) pyrochlore (Na0.33Ce0.67)2Ti2O7. With replacement of a fraction of the Ti reagent by Sn(IV) acetate, tin doping is possible in the pyrochlore. The materials have all been assessed for their use in catalysis by performing temperature programmed reduction (TPR) experiments under dilute hydrogen flow. The cerium-bismuth oxides show large and apparently reversible hydrogen uptake, but in situ powder X-ray diffraction shows that this is accompanied by phase separation into bismuth metal and CeO2 that occurs over 5 or more TPR cycles. In contrast, the cerium (IV) titanate pyrochlore shows reversible reduction at low temperature (150 ºC, after an activation step), which gives the material potential use as a precious metal support for catalysis: such as in the water-gas-shift reaction. Although Sn doping lowers the onset of reduction of the pyrochlore, consistent with an expanded lattice, the materials suffer from collapse to give SnO.

A facile anodic electrophoretic deposition (EPD) process has been developed to prepare thin uniform films consisting of titanate nanotubes (TNTs) that were synthesized by a hydrothermal approach. Such an EPD process offers easy control in the film thickness and the adhesion to the substrate was found to be strong. The chemical composition and structure of the products have been characterized by HRTEM, FESEM, XRD and TG/DTA. It was found that the functionalization of TNTs plays a key role on the electrolyte stability and the successful formation of a uniform TNT film with good adhesion. The as-prepared TNT films show exceptional superhydrophilic behavior with ultra-fast spreading, while it converts to superhydrophobicity yet with high adhesion after 1H,1H,2H,2H-perfluorooctyl-triethoxysilane modification. This study provides an interesting method to prepare films with extremely high wettability contrast that are useful for producing different kinds of functional materials.

The pressure-temperature (p-T) phase diagram of NH3BH3 has been investigated by thermal conductivity measurements up to 1.5 GPa at temperatures between 100 and 300 K, and the phase boundaries between the three known structural phases have been identified. The transformation between the room temperature tetragonal I4mm phase and the low temperature orthorhombic Pmn21 phase (Tc = 218 K at p = 0) shows only a small hysteresis. The transformation into the high pressure orthorhombic Cmc21 phase (at 1.0 GPa near 292 K) has a very strong hysteresis, up to Δp = 0.5 GPa, and below 230 K a fraction of this phase is metastable even at atmospheric pressure.

The stability of several kinds of substrates, such as Corning #1737 glass, fused silica, synthetic silica, water free synthetic silica, zinc selenide, silicon, and diamond like carbon (DLC) coated Si in supercritical water (663K and 25MPa) were examined. Their reaction with the water was evaluated by using Fourier transform infrared (FT-IR) spectroscopy. As a result of the present experiment, it was found that DLC-coated Si is one of the most stable and useful substrates for IR spectroscopy in supercritical water.