Thermal Annealing Behavior of Si-DLC Ibad Coatings

Published online by Cambridge University Press:  03 September 2012

C. G. Fountzoulas ,
J. D. Demaree ,
L. C. Sengupta  and
J. K. Hirvonen
C. G. Fountzoulas
Affiliation:
Weapons & Materials Research Directorate, Army Research Laboratory, APG, MD 21005-5069, [email protected]
J. D. Demaree
Affiliation:
Weapons & Materials Research Directorate, Army Research Laboratory, APG, MD 21005-5069, [email protected]
L. C. Sengupta
Affiliation:
Weapons & Materials Research Directorate, Army Research Laboratory, APG, MD 21005-5069, [email protected]
J. K. Hirvonen
Affiliation:
Weapons & Materials Research Directorate, Army Research Laboratory, APG, MD 21005-5069, [email protected]
Get access

Abstract

Amorphous, 700 nm thick, diamond-like carbon coatings containing silicon (Si-DLC), farmed by Ar+ ion beam assisted deposition (IBAD) on silicon substrates, were annealed in air at temperatures ranging from room temperature to 600°C for 30 minutes. RBS analysis showed that the composition of the films remained the same up to 200°C, but at higher temperatures the Si-DLC coatings began to oxidize at the outer surface of the coating, forming a surface layer of SiO2. After in-air annealing at 600°C the coating had been completely converted to SiO2, with no trace of carbon seen by RBS. FTIR spectra of the unannealed coatings showed a very broad mode typical of Si-DLC bonding as well as some absorption features associated with Si and SiO2. Above 200°C the transmission mode shifted to higher frequencies which may be caused by the growth of SiO2 and the decrease of the Si-DLC film thickness. The room temperature ball-on-disk friction coefficient of the coating against a 1/2′′ diameter 440 C steel ball at 1 N load ranged from 0.2 for the original coating up to 0.5 after a 100° anneal and returned to 0.2 after annealing at 200–400°C and fell to 0.12 after a 500°C exposure. The average Knoop microhardness (uncorrected for substrate effects) was 10 GPa (1,000 KHN) for coatings annealed at temperatures as high as 400°C. All coatings up to 500 °C passed the qualitative “Scotch Tape” test.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 438: Symposium A – Materials Modificaton and Synthesis by Ion Beam… , 1996 , 587
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Enke, K., Dimingen, H. and Huebsch, H., Appl. Phys. Lett., 36, 291 (1980).Google Scholar
2. Hioki, T., Hibi, S. and Kawamoto, J., Surf. Coat. Technol., 46, 233 (1991).Google Scholar
3. Oguri, K. and Arai, T., J. Mater. Res., 7, 1313 (1992).Google Scholar
4. Fountzoulas, C. G., Demaree, J. D., Kosik, W. E., Franzen, W., Croft, W. and Hirvonen, J. K. in Beam- Solid Interactions (Mat. Res. Soc. Symp. Proc. 279, Pittsburgh, PA, 1993), pp. 645–650.Google Scholar
5. Müller, U., Hauert, R., Oral, B., Tobler, M., Surf. Coat. Technol., 367, 76–77 (1995).Google Scholar
6. Tamor, M. A. in “Applications of Diamonds and Related Materials”, Eds: Feldman, A., Tzeng, Y., Yarbrough, W. A., Yoshikawa, M., Murakawa, M., NIST Special Publication 885, 691 (1995).Google Scholar
7. Freire, F. L., Achete, C. A., Mariotto, G., Canteri, R., J. Vac. Sci. Technol. A, 12, 3048 (1994).Google Scholar
8. Asoka-Kumar, P., Dorfinan, V. F., Abraizov, M. G., Yan, D., Pollak, F. H., J. Vac. Sci. Technol. A, 13, 1044 (1995).Google Scholar
9. Müller, U. and Hauert, R. in Mat. Res. Soc. Symp. Proc. 434 (1996).Google Scholar
10. Doolittle, L. R., Nucl. Inst. Meth. B, 15, 227 (1986).Google Scholar
11. Stelmack, L. A. (Private Communication), Implant Sciences, Corp., Wakefield, MA.Google Scholar
12. Oral, B., Hauert, R., Müller, U., Ernst, K.-H., Diamond and Related Materials, 4, 482 (1995).Google Scholar