Defect Generation During Epitaxial Growth of CoSi2 on Miniature Sized (100) Si Substrate and its Effect on Electrical Properties

Published online by Cambridge University Press:  15 February 2011

Jeong Soo Byun ,
Jeong Min Seon ,
Jin Won Park ,
Hyunsang Hwang  and
Jae Jeong Kim-
Jeong Soo Byun
Affiliation:
UILSI Laboratory of LG Semicon Co. Ltd., 1, Hyangjeong-dong, Cheongju-si 360–480, Korea
Jeong Min Seon
Affiliation:
UILSI Laboratory of LG Semicon Co. Ltd., 1, Hyangjeong-dong, Cheongju-si 360–480, Korea
Jin Won Park
Affiliation:
UILSI Laboratory of LG Semicon Co. Ltd., 1, Hyangjeong-dong, Cheongju-si 360–480, Korea
Hyunsang Hwang
Affiliation:
UILSI Laboratory of LG Semicon Co. Ltd., 1, Hyangjeong-dong, Cheongju-si 360–480, Korea
Jae Jeong Kim-
Affiliation:
UILSI Laboratory of LG Semicon Co. Ltd., 1, Hyangjeong-dong, Cheongju-si 360–480, Korea
Get access

Abstract

Self-aligned silicide (salicide) formation of epitaxial CoSi2, using a Co/Ti bilayer, on linear oxide (SiO2) patterned (100)Si substrate has been investigated. Rapid thermal annealing (RTA) at 550°C resulted in the lateral encroachment of silicide in the Si under the edge of the oxide. After RTA at 900°C, even though an epitaxial CoSi2 layer was formed on the Si substrate, defects such as lateral encroachment and voids were generated under the edge of the oxide. It was found that such defects lead to device failure due to the deterioration of the gate oxide and the shallow junction.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 402: Symposium H – Silicide Thin Films-Fabrication, Properties and Applications , 1995 , 167
Copyright
Copyright © Materials Research Society 1996

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Lawrence, M., Dass, A., Fraser, D.B., and Wei, C.S., Appl. Phys. Lett. 58, 1308 (1991).Google Scholar
[2] Hsia, S.L., Tan, T.Y., Smith, P., and McGuire, G.E., J. Appl. Phys. 70, 7579 (1991).Google Scholar
[3] Vantomme, A., Nicolet, M.A., and Theodore, N.D., J. Appl. Phys. 75, 3882 (1994).Google Scholar
[4] Adams, D.P., Yalisove, S.M., and Englesham, D.J., J. Appl. Phys. 76, 5190 (1994).Google Scholar
[5] Murarka, S.P., Silicides for VLSI Applications, (Academic Press, N.Y., 1983).Google Scholar
[6] Byun, J.S., Kim, D.H., Kim, W.S., and Kim, H.J., J. Appl. Phys. 78, 1725 (1995).Google Scholar